Place of Origin: | Hefei, China |
---|---|
Brand Name: | FUYUN |
Certification: | ISO, GB, BV, SONCAP, ASTM |
Model Number: | 1.0MM |
Minimum Order Quantity: | 2000 square meters |
Price: | USD 0.85-2.55 square meters |
Packaging Details: | Woven Bags, 20GP loads 19 tons, 40HQ loads 25 tons |
Delivery Time: | 10Days |
Payment Terms: | L/C, D/A, D/P, T/T, Western Union, MoneyGram, Paypal |
Supply Ability: | 25 Tons per Day |
Length: | 100m/roll | Application: | Chemical Plant, Fish Tank, Fish Pond, Shrimp Pond,shrimp Tank, Fishpond Lining |
---|---|---|---|
Material: | HDPE, LDPE, Polyethylene, EVA, PVC | Function: | Anti Seepage, Temperature Control, Oxygenation, High Bearing Capacity |
Density: | 0.90~ 0.96 G/cm | Product Name: | GRI GM13 Standard Chemically Resistant Chemical Reaction Tank Geomembrane Fabric LDPE HDPE 1.0mm Thickness |
Certificate: | ASTM, ISO, GM13 | Origin: | Made In China |
High Light: | Chemically Resistant Geomembrane Fabric,Chemical Reaction Tank Geomembrane Fabric,GRI GM13 Standard Geomembrane Fabric |
GRI GM13 Standard Chemically Resistant Chemical Reaction Tank Geomembrane Fabric LDPE HDPE 1.0mm Thickness
GRI GM13 Standard Chemically Resistant Chemical Reaction Tank Geomembrane Fabric LDPE HDPE 1.0mm
Quick Detail:
Production Description:
Geomembrane are the low permeable synthetic membrane pond liners which are widely used for Farm. Geomembrane hdpe pond liner are made of finest quality HDPE with specially formulated, virgin polyethylene resin, combined with specified quantity carbon black, antioxidant, anti-aging agent and UV resistance components, which make our geomembrane hdpe pond liner with excellent resistance to UV radiation and is suitable for exposed conditions. Geomembrane hdpe pond liner are fabricated by automatic production lines and three layered pressing technology in accordance with GRI GM13 standard. Compared with traditional concrete, asphalt and compacted clay, Geomembrane have proven to be far more cost effective, environmentally safe, excellent durable, chemically resistant, fast deployment and easy transportation
Table1(a) – High Density Polyethylene (HDPE) Geomembrane -Smooth
Properties | Test | Test Value | Testing Frequency | ||||||||
Method | 30 mils | 40 mils | 50 mils | 60 mils | 80 mils | 100 mils | 120 mils | (minimum) | |||
Thickness (min. ave.) | D5199 | nom. | Nom. | Nom. | Nom. | Nom. | Nom. | Nom. | Per roll | ||
· lowest individual of 10 values | -10% | -10% | -10% | -10% | -10% | -10% | -10% | ||||
Density mg/l (min.) | D 1505/D 792 | 0.940 g/cc | 0.940 g/cc | 0.940 g/cc | 0.940 g/cc | 0.940 g/cc | 0.940 g/cc | 0.940 g/cc | 200,000 lb | ||
Tensile Properties (1) (min. ave.) | D 6693 | 20,000 lb | |||||||||
· | yield strength | Type IV | 63 lb/in. | 84 lb/in. | 105 lb/in. | 126 lb/in. | 168 lb/in. | 210 lb/in. | 252 lb/in. | ||
· | break strength | 114 lb/in. | 152 lb/in. | 190 lb/in. | 228 lb/in. | 304 lb/in. | 380 lb/in. | 456 lb/in. | |||
· | yield elongation | 12% | 12% | 12% | 12% | 12% | 12% | 12% | |||
· | break elongation | 700% | 700% | 700% | 700% | 700% | 700% | 700% | |||
Tear Resistance (min. ave.) | D 1004 | 21 lb | 28 lb | 35 lb | 42 lb | 56 lb | 70 lb | 84 lb | 45,000 lb | ||
Puncture Resistance (min. ave.) | D 4833 | 54 lb | 72 lb | 90 lb | 108 lb | 144 lb | 180 lb | 216 lb | 45,000 lb | ||
Stress Crack Resistance (2) | D5397 | 300 hr. | 300 hr. | 300 hr. | 300 hr. | 300 hr. | 300 hr. | 300 hr. | per GRI-GM10 | ||
(App.) | |||||||||||
Carbon Black Content (range) | D 4218 (3) | 2.0-3.0% | 2.0-3.0% | 2.0-3.0% | 2.0-3.0% | 2.0-3.0% | 2.0-3.0% | 2.0-3.0% | 20,000 lb | ||
Carbon Black Dispersion | D 5596 | note (4) | note (4) | note (4) | note (4) | note (4) | note (4) | note (4) | 45,000 lb | ||
Oxidative Induction Time (OIT) (min. ave.) (5) | 200,000 lb | ||||||||||
(a) | Standard OIT | D 3895 | 100 min. | 100 min. | 100 min. | 100 min. | 100 min. | 100 min. | 100 min. | ||
— or — | |||||||||||
(b) High Pressure OIT | D 5885 | 400 min. | 400 min. | 400 min. | 400 min. | 400 min. | 400 min. | 400 min. | |||
Oven Aging at 85°C (5), (6) | D 5721 | ||||||||||
(a) Standard OIT (min. ave.) - % retained after 90 days | D 3895 | 55% | 55% | 55% | 55% | 55% | 55% | 55% | per each | ||
— or — | formulation | ||||||||||
(b) High Pressure OIT (min. ave.) - % retained after 90 days | D 5885 | 80% | 80% | 80% | 80% | 80% | 80% | 80% | |||
UV Resistance (7) | D 7238 | ||||||||||
(a) Standard OIT (min. ave.) | D 3895 | N.R. (8) | N.R. (8) | N.R. (8) | N.R. (8) | N.R. (8) | N.R. (8) | N.R. (8) | per each | ||
— or — | formulation | ||||||||||
(b) High Pressure OIT (min. ave.) - % retained after 1600 hrs (9) | D 5885 | 50% | 50% | 50% | 50% | 50% | 50% | 50% |
Specification:
general parameter:
Thickness | 0.15-3.0mm & customer ' s requirement |
Width | 1-8m & customer ' s requirement |
Length | 50-200m & customer ' s requirement |
Material | HDPE |
Color | Black,White,Green,Blue & customer ' s requirement |
Surface | Smooth |
Package | Double layers woven bag, and add two strap & customer ' s requirement |
Shipping Marks | support |
Production Standard | GRI,ASTM,GB or other standard |
specific parameter:
Item | Properties | Unit | Thickness | |||||||
1 | Thickness | mm | 0.25 | 0.35 | 0.5 | 0.75 | 1 | 1.25 | 1.5 | 2 |
2 | Density≧ | g/m3 | 0.94 | |||||||
3 | Stretch Yield Strength (horiz & vet)≧ | N/mm | 3.75 | 5 | 7.5 | 11 | 15 | 18 | 22 | 29 |
4 | Stretch Break Strength (horiz & vet)≧ | N/mm | 6.75 | 13.5 | 19 | 20 | 27 | 33 | 40 | 53 |
5 | Yield Elongation (horiz & vet)≧ | % | 12 | |||||||
6 | Break elongation (horiz & vet)≧ | % | 700 | |||||||
7 | Angle Tear Strength (horiz & vet)≧ | N | 31.25 | 45 | 62.5 | 93 | 125 | 156 | 187 | 249 |
8 | Puncture Strength | N | 80 | 150 | 160 | 240 | 320 | 400 | 480 | 640 |
9 | Stress Crack Resistance | Hrs | 300 | |||||||
10 | Carbon Black Content (range) | % | 2.0-3.0 | |||||||
11 | Carbon Black Dispersion | / | not more than 1 case grade 3 in 10 samples, grade 4 & 5 is not allowed | |||||||
12 | Oxidation Induction Time(OIT) | Standard OIT | ≧ 100 min | |||||||
High Pressure OIT | ≧ 400 min | |||||||||
13 | Thermal Aging at 85℃ | Standard OIT(min.ave.) retained after 90 days | 55% | |||||||
High Pressure OIT(min.ave.) retained after 90 days | 80% | |||||||||
14 | UV Resistance | Standard OIT (min.ave.) | 50% | |||||||
High Pressure OIT (min.ave.) retained after 1600 hrs | 50% | |||||||||
Application:
1, Aquaculture: factory breeding pool, fish pond, shrimp ponds circle of lining, sea cucumber, slope protection, etc.;
Advantage:
Package:
Packaging Details:
Neutral package of Pond Liner Material
Roll Size: 4m-7.0m
Or packed according to customers' requirements such as mark the company Logo
As example:
Specification 20ft container 40ft container
0.5mm 5.8/7*420m/roll 16rolls/38976m2 19rolls/55860m2
0.75mm 5.8/7*280m/roll 16rolls/25984m2 19rolls/37240m2
1mm 5.8/7*210m/roll 16rolls/19488m2 19rolls/27930m2
1.5mm 5.8/7*140m/roll 16rolls/12992m2 19rolls/18620m2
2.0mm 5.8/7*105m/roll 16rolls/9744m2 19rolls/13965m2
Factory Show:
Why Choose us?
FAQ: